CHS102
Electrode for General Stainless Steel |
AWS A5.4
E308-16
EN 1600 E 19 9 R 3 2
ISO 3581-A-E (19 9) R 3 2
ISO 3581-B-ES308-16
CSA W48-01 E308-16
JIS Z3221 D308-16
GB/T 983 E308-16 |
| |
|
|
Description:
CHS102
is a lime titanium type
welding rod for general stainless steels with all positions welding. Widely
be used for welding of 06Cr18Ni9 (e.g. 301、302、304、308) and Cr18Ni9Ti
stainless steel structures, which working temperature is below 300℃. Before
welding the rod should be baked at the temperature from 300℃ to 350℃ for 1
hour. Small current and short arc are recommended in welding and swaying
broad less than 2.5 times of diameter of the core rod is better.
|
Chemical
Composition of Deposited Metal(%)
|
|
C |
Mn |
Si |
Cr |
Ni |
Cu |
Mo |
S |
P |
|
Standard |
≤0.08 |
0.50-2.50 |
≤0.90 |
18.0-21.0 |
9.0-11.0 |
≤0.75 |
≤0.75 |
≤0.030 |
≤0.040 |
|
Typical |
0.048 |
0.86 |
0.66 |
19.88 |
9.70 |
0.23 |
0.14 |
0.012 |
0.028 |
Mechanical Properties of Deposited Metal
|
|
Tensile Strength Rm (MPa) |
Elongation A4 (%) |
|
Standard |
≥550 |
≥35 |
|
Typical |
595 |
44 |
Sizes, Pieces & Recommended Current Range
(AC or DC+)
|
Size (mm) |
2.0 x 300 |
2.5 x 300 |
3.2 x 350 |
4.0 x 400 |
5.0 x 400 |
|
Pieces (2kg) |
≈172 |
≈110 |
≈57 |
≈33 |
≈22 |
|
Current (A) |
F |
30-50 |
60-85 |
85-120 |
115-160 |
160-200 |
|
V, OH |
30-50 |
50-70 |
75-105 |
95-130 |
|