CHW-50C3
Solid Wire for MAG/MIG Welding |
AWS 5.18
ER70S-3
BS EN ISO 14341-A-G 38 4 M G2Si1
BS EN ISO 14341-B-G 49A 2 C G3
CSA W48-01 ER49S-3
JIS Z3312 YGW16
GB/T 8110 ER50-3 |
| |
|
|
Description:
CHW-50C3
is a coppered solid
wire for welding with mixture gas Ar+CO2. It shows a very good welding
performance especially in the range of lower current in case spark is much
lower than CHW-50C6SM (ER70S-6). Molten steel flows smoothly and weld seam
has a high crack-resistance. It is suitable for butt or fillet structures
made by mild steels and 500MPa tensile strength low alloy steels, in
particular for high speed welding sheet-steel, e.g. automobiles, railway
wagons, vehicles and locomotives.
|
Chemical
Composition of Wire (%)
|
|
C |
Mn |
Si |
S |
P |
|
Standard |
0.06-0.15 |
0.90-1.40 |
0.45-0.75 |
≤0.035 |
≤0.025 |
|
Typical |
0.074 |
1.01 |
0.62 |
0.011 |
0.015 |
|
|
Ni |
Cr |
Mo |
V |
Cu |
|
Standard |
≤0.15 |
≤0.15 |
≤0.15 |
≤0.03 |
≤0.50 |
|
Typical |
0.021 |
0.020 |
0.007 |
0.010 |
0.11 |
Mechanical Properties of Deposited Metal (AW)
|
|
Yield Point
ReL
(MPa) |
Tensile Strength
Rm (MPa) |
Elongation
A4 (%) |
Impact Value (J) -20℃ |
Shield Gas |
|
Standard |
≥400 |
≥480 |
≥22 |
≥27 |
20%CO2+80%Ar |
|
Typical |
435 |
540 |
30 |
120 |
Recommended Current Range
(DC+)
|
Diameter（mm） |
0.8 |
0.9 |
1.0 |
1.2 |
1.6 |
|
Current Range（A） |
60-150 |
60-200 |
70-230 |
100-350 |
120-450 |
|
Approvals |
CWB |
CE |
DB |
TUV |
|
Grade |
ER49S-3 |
EN 13479 EN 440 |
G2Si1 DIN EN440 |
EN440-G38 4 M G2Si1 |
|