Flux Cored Wire
   
Flux Cored Wire  药芯焊丝                                        
Item Code Equivalent Norm Welding Position Current Standard & Typical Chemical Composition of Deposited Metal (%)       Standard & Typical Mechanical Properties of Deposited Metal Applications Approvals
C Mn Si S P Cr Ni Mo V Postweld Condition Yield Point       ReL (MPa) Tensile Strength   
Rm (MPa)		 Elongation    
A4 (%)		 Akv Value (J) Shield Gas
Temp.(℃) Joule
CHT611 AWS A5.20 E61T-GC                         BS EN ISO  17632 T352PC1H10 F,VD,   OH,H DC+ — ≤1.75 ≤0.90 ≤0.03 ≤0.03 — — — — AW  ≥330 430-600 ≥22 0 ≥47  120 CO2  Suitable for all position as well as vertical down welding for mild steel structures. —
0.055 0.90 0.30 0.008 0.02 — — — — 430 505 29 -20 100
CHT701 AWS A5.20 E70T-1C                          BS EN ISO  17632 T422RC3H10 F,HF DC+ ≤0.12 ≤1.75 ≤0.90 ≤0.03 ≤0.03 — — — — AW ≥390 490-670 ≥22 -20 ≥22   70 CO2  It is suitable for flat or horizontal filler of structures fabricated by thick or medial thick armor plate with 490MPa grade tensile strength.  —
0.06 1.40 0.45 0.011 0.018 — — — — 450 545 28
CHT70B AWS A5.20 E70T-5C                          BS EN ISO  17632 T423BC3H5 F,HF,V DC+ ≤0.12 ≤1.75 ≤0.90 ≤0.03 ≤0.03 — — — — AW ≥390 490-670 ≥22 -30 ≥27
150		 CO2  It is suitable for flat or horizontal filler of higher tensile, better crack resisting mild steel structures fabricated by 490MPa grade tensile strength steels. Also it could be vertical up welding on which angle below 45°. —
0.07 1.50 0.50 0.013 0.018 — — — — 435 545 28
CHT70BM  AWS A5.20 E70T-5M                           BS EN ISO  17632 T423BM3H5
 		 F,HF,V DC+ ≤0.12 ≤1.75 ≤0.90 ≤0.03 ≤0.03 — — — — AW ≥390 490-670 ≥22 -30 ≥27
150		 75-80%Ar + balance CO2 It is suitable for flat or horizontal filler of higher tensile, better crack resisting mild steel structures fabricated by 490MPa grade tensile strength steels. Also it could be vertical up welding on which angle below 45°. —
0.07 1.46 0.50 0.013 0.018 — — — — 450 550 28
CHT711 AWS A5.20 E71T-1C                            BS EN ISO  17632 T422PC1H10 F,VD,   OH,H DC+ ≤0.12 ≤1.75 ≤0.90 ≤0.03 ≤0.03 — — — — AW ≥390 490-670 ≥22 0 125 CO2  It is widely used in structures fabricated by mild steel and 490MPa grade tensile strength steel, such as ships, pressure vessels, machinery, bridges, etc. CCS,LR,ABS,BV,GL,DNV, NK,BKI,CWB
0.055 1.35 0.40 0.009 0.018 — — — — 440 535 32 -20 ≥27  110
CHT711M AWS A5.20 E71T-1M                            BS EN ISO  17632 T422PM1H10 F,VD,     OH,H DC+ ≤0.12 ≤1.75 ≤0.90 ≤0.03 ≤0.03 — — — — AW ≥390 490-670 ≥22 -20 ≥27  75-80%Ar + balance CO2 It is widely used in structures fabricated by mild steel and 490MPa grade tensile strength steel, such as ships, pressure vessels, machinery, bridges and so on. —
0.055 1.3 0.40 0.009 0.018 — — — — 440 540 30   120
CHT71Ni AWS A5.20 E71T-1C-J                           BS EN ISO  17632 T424PC1H10
 		 F,V,   OH,H DC+ ≤0.12 ≤1.75 ≤0.90 ≤0.03 ≤0.03 — ≤0.5 — — AW ≥390 490-670 ≥22 -40 ≥27
80		 CO2  Suitable for structures fabricated by mild steel or 490MPa grade tensile strength steels, such as pressure vessels, ships, offshore drilling platforms, pipelines and so on.  —
0.04 1.30 0.35 0.015 0.02 — 0.45 — — 425 520 30
CHT71Ni1 BS EN ISO  17632 T4231NiPC1H10 F,V,   OH,H DC+ ≤0.12 ≤1.50 ≤0.80 ≤0.03 ≤0.03 — 0.8-1.10 — — AW ≥400 490-620 ≥20 -30 ≥27
110		 CO2  Suitable for structures fabricated by mild steel or 490MPa grade tensile strngth steels, such as pressure vessels, offshore drilling platforms, pipelines and so on.  —
0.05 1.2 0.35 0.006 0.015 — 0.95 — — 440 520 30
CHT80B  AWS A5.29 E80T5-GC                                                         BS EN ISO  17632 T463BC3H5
 		 F,HF,V DC+ — ≥1.0 — ≤0.03 ≤0.03 — — — — AW ≥470 550-690 ≥19 -30 ≥27
150		 CO2  It is suitable for flat, horizontal filler or vertical up welding on which angle below 45°, higher tensile, better crack-resisting structures that fabricated by 550MPa grade tensile strength, heat resistant low alloy steels, such as ships, pressure vessels of petroleum chemical, bridges, etc. —
0.07 1.5 0.5 0.013 0.018 — 0.2 — — 480 560 30
CHT80B2B AWS A5.29 E80T5-B2C
ISO 17634 T(CrMo1)BC3H5
 		 F,HF,V DC+ 0.05-0.12 ≤1.25 ≤0.80 ≤0.03 ≤0.03 1.0-1.5 — 0.4-0.65 — PWHT ≥470 550-690 ≥19 25 ≥47
180		 CO2  It is suitable for flat, horizontal filler or vertical up welding on which angle below 45°, higher tensile strength, better crack-resisting structures that fabricated by 550MPa grade heat resistant low alloy steels, which work temperature lower than 520℃.Welded piece should be preheated to 150-300℃ before welding. —
0.06 0.80 0.30 0.010 0.012 1.15 — 0.45 — 690℃X1h 510 600 24
CHT81B2 AWS A5.29 E81T1-B2C
ISO 17634 T(CrMo1)PC1H10
 		 F,V,   OH,H DC+ 0.05-0.12 ≤1.25 ≤0.80 ≤0.03 ≤0.03 1.0-1.5 — 0.4-0.65 — PWHT ≥470 550-690 ≥19 25 ≥27
75		 CO2  Suitable for welding 550MPa grade heat resistant low alloy steel structures,which work temperature lower than 520℃, e.g.15CrMoR (1%Cr-0.5%Mo). Welded piece should be preheated to 150-300℃ before welding. —
0.058 0.80 0.25 0.01 0.011 1.15 — 0.45 — 690℃X1h 550 630 23
CHT81B2M AWS A5.29 E81T1-B2M
ISO 17634 T(CrMo1)PM1H10
 		 F,V,   OH,H DC+ 0.05-0.12 ≤1.25 ≤0.80 ≤0.03 ≤0.03 1.0-1.5 — 0.4-0.65 — PWHT ≥470 550-690 ≥19 25 ≥27
100		 75-80%Ar + balance CO2 Suitable for welding 550MPa grade heat resistant low alloy steel structures,which work temperature lower than 520℃, e.g.15CrMoR (1%Cr-0.5%Mo). Welded piece should be preheated to 150-300℃ before welding. —
0.06 0.80 0.25 0.01 0.011 1.15 — 0.45 — 690℃X1h 555 635 24
CHT81B2V DGS K1801.01-2006 F,V,
OH,H		 DC+ ≤0.12 ≤1.50 ≤0.90 ≤0.03 ≤0.03 1.0-1.5 — 0.4-0.65 0.1-0.35 PWHT ≥470 ≥550 ≥19 25 ≥27
70		 CO2  Suitable for welding 550MPa grade heat resistant low alloy pearlitic steel structures, which work temperature below 540℃, e.g.12Cr1MoVR. Welded piece should be preheated to 150-300℃ before welding. —
0.055 0.80 0.25 0.01 0.011 1.15 — 0.45 0.15 730℃X2h 540 640 22
CHT81B6 AWS A5.29 E81T1-B6C
                                                      ISO 17634 T(CrMo5)PC1H10
 		 F,V,
OH,H		 DC+ 0.05-0.12 ≤1.25 ≤1.0 ≤0.03 ≤0.04 4.0-6.0 ≤0.40 0.4-0.65 Cu≤0.50 PWHT ≥470 550-690 ≥19 25 ≥27
95		 CO2  It is suitable for fabricate structures made by 550MPa grade Cr5Mo steel. Welded piece should be preheated to 150-300℃ before welding. —
0.06 0.75 0.25 0.01 0.011 4.2 0.015 0.52 0.02 745℃X2h 530 640 20
CHT81K2 AWS A5.29 E81T1-K2C                     BS EN ISO  17632 T4631.5NiPC1H10
 		 F,V,
OH,H		 DC+ ≤0.15 0.5-1.75 ≤0.80 ≤0.03 ≤0.03 ≤0.15 1.0-2.0 — — AW ≥470 550-690 ≥19 -30 ≥27
111		 CO2  It is used in structures fabricated by 550MPa grade tensile strength steel, such as ships, pressure vessels, machinery, bridges, offshore drilling platforms and so on. —
0.05 1.35 0.35 0.008 0.017 0.02 1.45 — — 495 580 28
CHT81Ni1 AWS A5.29 E81T1-Ni1C
                                                           BS EN ISO  17632 T4631NiPC1H10
 		 F,V,
OH,H		 DC+ ≤0.12 ≤1.50 ≤0.80 ≤0.03 ≤0.03 — 0.80-1.10 ≤0.35 — AW ≥470 550-690 ≥19 -30 ≥27
90		 CO2  It is used in structures fabricated by 550MPa grade tensile strength steel, such as ships, pressure vessels, machinery, bridges, petrochemical industry and so on. —
0.055 1.35 0.35 0.005 0.015 — 0.95 0.10 — 520 605 25
CHT81Ni1M AWS A5.29 E81T1-Ni1M                  BS EN ISO  17632 T4631NiPM1H10 F,V,
OH,H		 DC+ ≤0.12 ≤1.50 ≤0.80 ≤0.03 ≤0.03 — 0.80-1.10 ≤0.35 — AW ≥470 550-690 ≥19 -30 ≥27
95		 75-80%Ar + balance CO2 It is used in structures fabricated by 550MPa grade tensile strength steel, such as ships, pressure vessels, machinery, bridges, petrochemical industry and so on. —
0.053 1.37 0.40 0.006 0.013 — 0.99 0.11 — 530 610 27
CHT81Ni2 AWS A5.29 E81T1-Ni2C                   BS EN ISO  17632 T4642NiPC1H10 F,V,
OH,H		 DC+ ≤0.12 ≤1.50 ≤0.80 ≤0.03 ≤0.03 — 1.75-2.75 — — AW ≥470 550-690 ≥19 -40 ≥27
90		 CO2  It is used in structures fabricated by 550MPa grade tensile strength steel, such as ships, pressure vessels, machinery, bridges, petrochemical industry, offshore drilling platforms, etc. —
0.05 1.30 0.35 0.008 0.017 — 2.20 — — 485 580 28
CHT90B3B AWS  A5.29  E91T5-B3C                         ISO 17634 T(CrMo2)BC3H5 F,HF,V DC+ 0.05-0.12 ≤1.25 ≤0.80 ≤0.03 ≤0.03 2.0-2.5 — 0.90-1.20 — PWHT ≥540 620-760 ≥17 25
150		 CO2  Suitable for welding 600MPa grade 25%Cr-1%Mo heat resistant low alloy steel structures, which work temperature below 550℃, such as high temperature, high pressure pipes, chemical industry equipment, petroleum thermal cracking equipment, etc. Welded piece should be preheated to 150-300℃ before welding. —
0.06 0.80 0.30 0.01 0.018 2.15 — 1.08 — 690℃X1h 565 660 21
CHT91B3 AWS  A5.29  E91T1-B3C                          ISO 17634 T(CrMo2)PC1H10 F,V,
OH,H		 DC+ 0.05-0.12 ≤1.25 ≤0.80 ≤0.03 ≤0.03 2.0-2.5 — 0.90-1.20 — PWHT ≥540 620-760 ≥17 25 ≥27
60		 CO2  Suitable for welding 600MPa grade 25%Cr-1%Mo (12Cr2Mo1R) heat resistant low alloy steel structures, which work temperature below 550℃, such as high temperature, high pressure pipes, chemical industry equipment, petroleum thermal cracking equipment, etc. Welded piece should be preheated to 150-300℃ before welding.  —
0.06 0.80 0.25 0.012 0.018 2.26 — 1.06 — 690℃X1h 600 730 20
CHT91K2 AWS  A5.29  E91T1-K2C                      BS EN ISO  17632 T5021.5NiPC1H10 F,V,
OH,H		 DC+ ≤0.15 0.5-1.75 ≤0.80 ≤0.03 ≤0.03 ≤0.15 1.0-2.0 ≤0.35 ≤0.05 AW ≥540 620-760 ≥17 -20 ≥27
70		 CO2  Suitable for welding structures fabricated by 600MPa grade tensile strength steel, such as ships, pressure vessels, machineries, petroleum & chemical industries, bridges etc.   —
0.05 1.45 0.40 0.013 0.018 0.022 1.55 0.13 0.012 560 650 23

 

   

 
 
  

 


Copyright © 2000 Atlantic China Welding Consumables, Inc. All rights reserved.
Send mail to webmaster@chinaweld-atlantic.com with questions or comments about this web site.