TIG Wires
|
| |
|
|
Solid Wire for TIG Welding 钨极惰性气体保护焊实芯焊丝 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Item Code |
Equivalent Norm |
Welding Position |
Current |
Chemical Composition of Wire (%, Typical) |
Mechanical Properties of Deposited Metal (Typical) |
Application |
|
C |
Mn |
Si |
S |
P |
Cr |
Ni |
Mo |
Cu |
Others |
Postweld Condition |
Yield Point
ReL (MPa) |
Tensile Strength
Rm (MPa) |
Elongation A4(%) |
Akv Value (J) |
Shield Gas |
|
Temp.(℃) |
Joule |
|
CHG-308 |
AWS A5.9 ER308 BS EN ISO
14343-B-SS308 JIS Z3321 Y308 |
F,V,
OH,H |
DC |
0.05 |
1.79 |
0.48 |
0.013 |
0.022 |
19.72 |
9.40 |
0.005 |
0.06 |
— |
AW |
— |
580 |
42 |
— |
— |
Ar |
For Cr18Ni8, Cr18Ni12, Cr20Ni10 austenitic stainless steels, such as 301
,302 & 308, etc. especially 304. |
|
CHG-308L |
AWS A5.9 ER308L BS EN ISO 14343-A-W(19
9 L) BS EN ISO 14343-B-SS308L JIS Z3321
Y308L |
F,V,
OH,H |
DC |
0.024 |
1.72 |
0.48 |
0.010 |
0.018 |
19.76 |
9.83 |
0.006 |
0.06 |
— |
AW |
— |
560 |
45 |
— |
— |
Ar |
Suitable for extra-low carbon 00Cr19Ni10 structures. Also it could fabricat
0Cr18Ni10Ti structures, which working temperature lower than 300℃.
E.g. synthetic fibre, fertilizer & chemical industrial equipment and so on. |
|
CHG-309 |
AWS A5.9 ER309 BS EN ISO 14343-A-W(22 12
H) BS EN ISO 14343-B-SS309 JIS Z3321 Y309 |
F,V,
OH,H |
DC |
0.06 |
2.05 |
0.34 |
0.011 |
0.020 |
23.83 |
13.26 |
0.008 |
0.06 |
— |
AW |
— |
580 |
39 |
— |
— |
Ar |
Suitable for welding similar chemical composition stainless steel structures
and dissimilar steel, e.g. Cr19Ni10 with mild steel, as well as for welding
high Mn and High Cr steels. |
|
CHG-309L |
AWS A5.9 ER309L BS EN ISO 14343-A-W(23 12
L) BS EN ISO 14343-B-SS309L JIS Z3321 Y309L |
F,V,
OH,H |
DC |
0.026 |
2.11 |
0.38 |
0.008 |
0.017 |
23.56 |
12.31 |
0.006 |
0.07 |
— |
AW |
— |
570 |
38 |
— |
— |
Ar |
For welding extra low carbon stainless steel structures with sililar
chemical composition, such as synthetic fibre, petrochemical equipment as
well as nuclear reactor. Also it could be used for dissimilar steel welding. |
|
CHG-310 |
AWS A5.9 ER310 BS EN ISO 14343-A-W(25
20) BS EN ISO 14343-B-SS310 JIS Z3321 Y310 |
F,V,
OH,H |
DC |
0.09 |
1.65 |
0.53 |
0.015 |
0.021 |
25.81 |
20.34 |
0.020 |
0.08 |
— |
AW |
— |
610 |
38 |
— |
— |
Ar |
For welding Cr25Ni20 stainless steels structures, which provide good
oxidation corrosion resistance and heat resistance. Also it could be used
for dissimilar steel welding and for welding high Cr, high Mn steels. |
|
CHG-316 |
AWS A5.9 ER316 BS EN ISO
14343-B-SS316 JIS Z3321 Y316 |
F,V,
OH,H |
DC |
0.04 |
1.71 |
0.52 |
0.009 |
0.018 |
18.54 |
11.50 |
2.18 |
0.08 |
— |
AW |
— |
600 |
31 |
— |
— |
Ar |
Mainly for welding structures in chemical industry and power engineering
that made by Cr19Ni12Mo2 stainless steels such as AISI316,SUS316. Also it
could be used for structures made by high Cr steel and dissimilar steels,
which do not need to PWHT. |
|
CHG-316L |
AWS A5.9 ER316L BS EN ISO 14343-A-W(19 12 3
L) BS EN ISO 14343-B-SS316L JIS Z3321 Y316L |
F,V,
OH,H |
DC |
0.025 |
1.71 |
0.48 |
0.009 |
0.018 |
18.54 |
11.50 |
2.18 |
0.09 |
— |
AW |
— |
580 |
32 |
— |
— |
Ar |
Mainly for welding structures in chemical industry and power engineering
that made by 00Cr19Ni12Mo2 stainless steels such as AISI316L,SUS316L. Also
it could be used for structures made by high Cr steel and dissimilar steels,
which do not need to PWHT. |
|
CHG-321 |
AWS A5.9 ER321 BS EN ISO
14343-B-SS321 JIS Z3321 Y321 |
F,V,
OH,H |
DC |
0.028 |
1.85 |
0.45 |
0.010 |
0.021 |
18.92 |
9.25 |
0.007 |
0.08 |
Ti 0.34 |
AW |
— |
575 |
40 |
— |
— |
Ar |
It is suitable for welding structures made by 1Cr18Ni9Ti austenitic
stainless steel as well as the one with similar composition. |
|
CHG-347 |
AWS A5.9 ER347 BS EN ISO 14343-A-W(19 9 Nb)
BS EN ISO 14343-B-SS347 JIS Z3321 Y347 |
F,V,
OH,H |
DC |
0.05 |
1.81 |
0.51 |
0.008 |
0.021 |
20.01 |
10.10 |
0.009 |
0.12 |
Nb 0.59 |
AW |
— |
585 |
39 |
— |
— |
Ar |
It is suitable for welding structures made by 1Cr18Ni11Nb austenitic
stainless steel as well as the one with similar composition. |
|
CHG-410 |
AWS A5.9 ER410
BS EN ISO
14343-A-G(13) BS EN ISO
14343-B-SS410 JIS Z3321 Y410 |
F,V,
OH,H |
DC |
0.06 |
0.47 |
0.38 |
0.012 |
0.011 |
12.90 |
0.20 |
Nb0.81 |
0.17 |
— |
AW |
— |
540 |
35 |
— |
— |
Ar |
Suitable for Cr13 stainless steels. The base metal should be tempered
at 850℃ for 2 hours after
welding. |
|
CHG-52 |
AWS A5.18 ER70S-2 BS EN 1668-W 38 3 W2Ti
ISO 636-A-W 38 3 W2Ti ISO 636-B-W 49A 3 W2 |
F,V,
OH,H |
DC |
0.035 |
1.14 |
0.53 |
0.004 |
0.011 |
— |
Al 0.08 |
Zr 0.08 |
0.20 |
Ti 0.13 |
AW |
450 |
550 |
26 |
-30 |
85 |
Ar |
Suitable for single-pass or multi-pass welding structures fabricated by
500MPa grade killed steels, balanced steels and boiling steels. No meed to
shield gas in another side of the seam. |
|
CHG-52T |
AWS A5.18 ER70S-G JIS Z3316 YGT50 |
F,V,
OH,H |
DC |
0.090 |
1.45 |
0.78 |
0.012 |
0.014 |
— |
— |
— |
0.14 |
Ti 0.17 |
AW |
440 |
560 |
30 |
-30 |
75 |
Ar |
Widely used for structures fabricated by 500-550MPa tensil strength low
alloy steels of X60,X65,X70,18Nb and 12～16Mn
etc. such as bridges,heavy engineering machinary, vehicles, skyscrapers,
petroleum & chemical industry equipment and so on. |
|
CHG-53 |
AWS A5.18 ER70S-3 BS EN 1668-W 38 4
W2Si ISO 636-A-W 38 4 W2Si ISO 636-B-W 49A 4
W3 JIS Z3316 YGT50 |
F,V,
OH,H |
DC |
0.099 |
1.11 |
0.62 |
0.011 |
0.015 |
0.020 |
0.021 |
0.007 |
0.18 |
V 0.08 |
AW |
435 |
540 |
29 |
-40 |
120 |
Ar |
For structures fabricated by 500MPa grade tensil strength mild steels or low
alloy steels, e.g. bridges, vehicles and so on. |
|
CHG-54 |
AWS A5.18 ER70S-4 BS EN 1668-W 382
W2Si ISO 636-A-W 382 W2Si ISO
636-B-W 49A2 W4 JIS Z3316 YGT50 |
F,V,
OH,H |
DC |
0.099 |
1.10 |
0.72 |
0.015 |
0.016 |
0.022 |
0.021 |
0.007 |
0.22 |
V 0.010 |
AW |
410 |
530 |
29 |
-20 |
100 |
Ar |
For structures fabricated by 500MPa grade tensil strength mild steels or low
alloy steels, e.g. bridges, vehicles and so on. |
|
CHG-55B2 |
AWS A5.28 ER80S-B2 BS EN ISO 21952-A-W
(CrMo1Si) BS EN ISO 21952-B-W 1CM3 JIS Z3316 YGT1CM |
F,V,
OH,H |
DC |
0.076 |
1.15 |
0.67 |
0.007 |
0.015 |
1.25 |
— |
0.50 |
0.20 |
— |
AW |
505 |
620 |
23 |
25 |
80 |
Ar |
Suitable for structures fabricated by 1.25Cr-0.5Mo series pearlitic
heat-resisting low alloy steels such as high press steam pipes of boiler or
steam turbine which work temperature is lower than 510℃. |
|
CHG-55B2V |
AWS A5.28 ER80S-G |
F,V,
OH,H |
DC |
0.080 |
1.35 |
0.70 |
0.010 |
0.012 |
1.25 |
— |
0.58 |
0.20 |
V 0.27 |
AW |
515 |
640 |
22 |
25 |
85 |
Ar |
Suitable for structures fabricated by 1.25Cr-0.5Mo-0.2%V series pearlitic
heat-resisting low alloy steels such as high press steam pipes of boilers,
nuclear reactors, petrochemical equipments which work temperature is lower
than 510℃. |
|
CHG-55B6 |
AWS A5.28 ER80S-B6 BS EN ISO 21952-A-W
CrMo5Si BS EN ISO 21952-B-W (5CM) JIS Z3316
YGT5CM |
F,V,
OH,H |
DC |
0.080 |
1.14 |
0.65 |
0.009 |
0.013 |
5.10 |
— |
0.58 |
0.12 |
— |
PWHT 740℃X2h |
470 |
610 |
22 |
25 |
180 |
Ar |
It is widely used for superheaters, heat exchangers, pipes of industry
boilers as well as high pressure vessels that fabricated by 5％Cr-0.5％Mo
heat resisting low alloy steels. |
|
CHG-55C1 |
AWS A5.28 ER80S-Ni1 BS EN 1668-W 46 5
W3Ni1 ISO 636-A-W 46 5 W3Ni1 ISO 636-B-W 55A 5
WN2 |
F,V,
OH,H |
DC |
0.084 |
1.06 |
0.53 |
0.010 |
0.010 |
0.070 |
0.93 |
0.001 |
0.21 |
Ti 0.010 |
AW |
430 |
520 |
30 |
-45 |
200 |
Ar |
Suitable for structures fabricated by low alloys steels, which has low
temperature toughness and the working temperature of it around -45℃. |
|
CHG-56 |
AWS A5.18 ER70S-6 BS EN 1668-W 42 3 W3Si1
ISO 636-A-W 42 3 W3Si1 ISO 636-B-W 49A 3
W6 JIS Z3316 YGT50 |
F,V,
OH,H |
DC |
0.07 |
1.47 |
0.90 |
0.011 |
0.012 |
0.020 |
0.021 |
0.007 |
0.18 |
V 0.008 |
AW |
430 |
530 |
29 |
-30 |
90 |
Ar |
Suitable for single-pass or multi-pass welding for structures fabricated by
500MPa tensil strength mild steels or low alloy steels, e.g. vehicles,
containers, bridges, machinary and so on. |
|
CHG-62B3 |
AWS A5.28 ER90S-B3 BS EN ISO 21952-A-W
CrMo2Si BS EN ISO 21952-B-W (2C1M3) JIS Z3316
YGT2CM |
F,V,
OH,H |
DC |
0.09 |
0.92 |
0.65 |
0.006 |
0.013 |
2.30 |
0.002 |
1.04 |
0.27 |
— |
PWHT 690℃X1h |
575 |
680 |
23 |
25 |
90 |
Ar |
Suitable for structures fabricated by 2.25Cr-1Mo series heat-resisting low
alloy steels (T22/P22, 10CrMo910, STBA24/STPA24). Such as high press steam
pipes of boilers which work temperature is lower than 580℃. |
|
CHG-91 |
AWS A5.28 ER90S-B9 BS EN ISO 21952-B-W 9C1MV |
F,V,
OH,H |
DC |
0.084 |
0.92 |
0.18 |
0.006 |
0.006 |
9.09 |
Ni 0.70
Nb 0.07 |
Mo 1.06
Al 0.024 |
Cu 0.020
N 0.063 |
V 0.23 |
PWHT 755℃X1h |
590 |
680 |
20 |
25 |
80 |
Ar |
Suitable for superheaters and re-superheaters belong to subcritical,
critical or supercritical boilers, which fabricated by martensite
heat-resisting T/P91 alloy steel. The tensile strength in 630℃
high temperature achieves 340MPa. |
|
CHG-92 |
AWS A5.28 ER90S-G BS EN ISO 21952-A-W CrMoWV12Si |
F,V,
OH,H |
DC |
0.12 |
0.84 |
0.29 |
0.006 |
0.007 |
Cr 9.56
Co 0.88 |
Ni 0.62
Nb 0.067 |
Mo 0.64
Al 0.020 |
Cu 0.027
N 0.063 |
V 0.23
W 1.57 |
PWHT 760℃X4h |
660 |
755 |
24 |
25 |
210 |
Ar |
It is suitable for welding structures fabricated by high temperature
resisting low alloy steels such as 9％Cr-1.5％W-Mo-Nb-N,
T/P92 or NF616,and the structures have long service period under a working
temperature of 650℃. |
|
CHG-S5 |
AWS A5.18 ER70S-7 BS EN 1668-W 42 Z
W4Si1 ISO 636-A-W 42 Z W4Si1 ISO 636-B-W 49A
Z W12 |
F,V,
OH,H |
DC |
0.087 |
1.88 |
0.77 |
0.006 |
0.015 |
0.020 |
0.021 |
— |
0.14 |
— |
AW |
445 |
545 |
31 |
25 |
127 |
Ar |
Suitable for single-pass or multi-pass welding for structures fabricated by
500MPa tensil strength mild steels or low alloy steels, e.g. vehicles,
containers, bridges, machinary and so on. |
|
CHG-SH |
AWS A5.18 ER70S-G |
F,V,
OH,H |
DC |
0.10 |
1.45 |
0.89 |
0.005 |
0.011 |
0.020 |
0.048 |
0.002 |
0.16 |
— |
PWHT 620℃X1h |
390 |
510 |
32 |
-30 |
210 |
Ar |
It is suitable for pressure vessels of high temperature separators and
recycle hydrogen knockout drums that fabricated by 16Mn（HIC）steels. |
|
CHG-SH53 |
AWS A5.18 ER70S-G |
F,V,
OH,H |
DC |
0.11 |
1.17 |
0.66 |
0.005 |
0.012 |
0.028 |
0.020 |
0.008 |
0.20 |
V 0.009 |
AW |
410 |
520 |
33 |
-30 |
290 |
Ar |
It is suitable for pressure vessels of high temperature separators, recycle
hydrogen knockout drums that fabricated by 16MnR（HIC）steels.
Also it could be used for welding petroleum transmission pipe lines. |
|
CHG-SHA |
AWS A5.18 ER70S-G |
F,V,
OH,H |
DC |
0.09 |
1.11 |
0.52 |
0.002 |
0.004 |
0.020 |
0.021 |
0.100 |
0.20 |
Ti 0.020 |
AW |
415 |
530 |
30 |
-30 |
280 |
Ar |
It is suitable for pressure vessels of high temperature separators, recycle
hydrogen knockout drums that fabricated by 16MnR（HIC）steels.
Also it could be used for welding petroleum transmission pipe lines. |
|
CHG-NiCrMo-6 |
AWS A5.14 ERNiCrMo-6 JIS Z3334 YNiCrMo-6 |
F,V,
OH,H |
DC |
0.006 |
2.60 |
0.37 |
0.002 |
0.015 |
15.12 |
Balance |
5.80 |
Cu 0.07 Nb 1.08 |
Fe 1.46 W 1.33 |
AW |
440 |
640 |
40 |
-196 |
180 |
Ar |
Mainly for welding Nickel base alloys. Also it could be used for problem
alloys, copious cooling steels and dissimilar metals. |
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Diameter of ATLANTIC TIG wires from 1.6mm to 3.0mm and the length are
1,000mm |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Standard Packing: 5kg/hard plastic box, then 20kg (4 boxes)/carton, last
1,000kg (50 cartons)/wooden crate. |
|
|
|
|
|